Medthin™ 11 - Implants
A possible alternative to TiN - in line with existing predicates
Medthin™ 11 coating is known to reduce ion release from implant substrates materials such as CoCr, SS or TAV. The coating is applied with thickness of about 5µm and it has adhesion strength to metal substrates higher than 1.0GPa leading to an improved abrasion resistance when compared with uncoated CoCrMo. Titanium Niobium Nitride (TiNbN) is deposited with latest generation Ionbond technologies showing a polycrystalline cubic structure with a fine and very dense structure, roughness (Ra) values below 0.05µm, ideal for articulating zones. The coating coverage is rather uniform on external surfaces whereas for inner surfaces a Ionbond proprietary technology can be applied in some cases.
Ionbond can currently deliver coating service ”me too” of “Medthin™ 11 TiNbN on Implants” from Europe and Asia using large coating chambers at attractive prices.
Technical data
Material
Titanium Niobium Nitride
Application Reference
Othopaedic, spine & trauma
Color
Gold
Thickness range [µm]
3 - 7
Thickness range [µm]
3 - 7
Hardness, GPa
24 to 27
Adhesion (depending on material)
>1500
Wear reduction
>50%
Roughness Ra (Rz) as deposited
<50
Medthin™ 01 - Implants
A reference coating for implantsMedthin™ 01 coating is particularly suitable for improving articulating joints such as those of “Coating on UHMWPE” where polyethylene wear an…
Read more
Medthin™ 42 - Implants
Probably the best (hard) coating for implantsMedthin™ 42 coating combines high adhesion strength with low UHMWPE wear and nearly no ion release from the implant substrate rea…
Read more
Medthin™ 43 - Implants
The high class coating for implantsMedthin™ 43 coating is excellent to improve articulating joints such as those of “Coating on UHMWPE” where polyethylene wear and ion releas…
Read more
Medthin™ 60 - Implants
The high oxidation resistance coatingMedthin™ 60 coating is particularly suitable for improving articulating joints such as those of “Coating on UHMWPE” where polyethylene we…
Read more
Medthin™ 01 - Instruments
TiN coating for medical instrumentsMedthin™ 01 TiN, gold colour, has superior adhesion to the substrate materials with good chemical stability when undergoing several cleanin…
Read more
Medthin™ 04 - Instruments
TiON coating for use in hospital environmentMedthin™ 04 TiON, has “sand beach” color or gray color. The coating evidenced considerable reduction of colony-forming units (CFU)…
Read more
Medthin™ 10 - Instruments
TiCN coating for medical instruments & hospital hardwareMedthin™ 10 TiCN has carbon inside the TiN cubic matrix strengthening and conferring a pink colour to this coating…
Read more
Medthin™ 11 - Instruments
TiNbN light gold coatingMedthin™ 11 TiNbN, has slighter gold colour compared to TiN. It is very similar to TiN and ZrN in terms of structure and overall mechanical properties…
Read more
Medthin™ 16 - Instruments
TiAIN coating for surgical & dental instrumentsMedthin™ 16 TiAlN, the bronze colored Medthin™ 16 TiAlN’s high wear resistance and adhesion, excellent resistance to alkali…
Read more
Medthin™ 18 - Instruments
TiAICN coating for medical instruments & hospital hardwareMedthin™ 18 TiAlCN is a multi-layer coating with a TiCN top layer. The carbon in the top-layer of the coating ac…
Read more
Medthin™ 20 - Instruments
AITiN coating with great chemical barrier functionMedthin™ 20 AlTiN is widely used for the coating of medical instruments due to its anti-glare properties, superior adhesion …
Read more
Medthin™ 30 - Instruments
CrN coating for surgical & dental instrumentsMedthin™ 30 CrN, has silver-grey color, shows high fracture toughness, wear resistance and adhesion, making it an ideal coati…
Read more
Medthin™ 33 - Instruments
CrCN coating for all types of surgical instrumentsMedthin™ 33 CrCN, is a unique coating that combines the excellent adhesion and fracture toughness of CrN with the low light …
Read more
Medthin™ 36 - Instruments
MeDLC coating for surgical instrumentsMedthin™ 36 MeDLC, a black color coating with high abrasive and scratch resistance. Produced in large coating chambers, the process allo…
Read more
Medthin™ 40 - Instruments
MeDLC coating for complex shape partsMedthin™ 40 “Metal Diamond Like Carbon” , is a low surface roughness coating based on Carbon amorphous phase embedding the crystalline cr…
Read more
Medthin™ 41 - Instruments
DLC coating with improved scratch resistanceMedthin™ 41 DLC is a multilayer coating with a WCC base layer and a pure DLC (carbon) top layer. Such engineered structure confers…
Read more
Medthin™ 42 - Instruments
DLC coating for surgical instrumentsMedthin™ 42 DLC is a multilayer coating with a Chromium Nitride (CrN) base layer followed by a thin interlayer made of WCC and a top DLC …
Read more
Medthin™ 43 - Instruments
ADLC coating for surgical instrumentsMedthin™ 43 ADLC is a dual layer coating with a SiC base layer followed by top DLC (carbon) layer. The two layers confer to Medthin™ 43 …
Read more
Medthin™ 48 - Instruments
Medthin™ 48 tetragonal carbonMedthin™ 48 ta-C, a suitable coating for «fine» bone cutting applicable in small drills or general bone cutting tools.
Read more