CVD Coatings for Forming and Molding Tools

Explore the benefits of CVD coatings for increasing the durability and wear resistance of forming tools

Ionbond Forming Molding Portrait
Orbital forming tool white

Ionbond™ CVD coatings for the most demanding forming applications under harsh conditions

Chemical vapor deposition (CVD) is the oldest deposition technology for wear-resistant coatings for industrial forming applications. Modern CVD machines ensure robust and reliable operations and high yield rates. This has resulted in the popularity of CVD for certain applications, such as metal forming tools and extrusion dies. These tools are subject to harsh environmental conditions in terms of abrasive and adhesive wear as well as oxidation and corrosion, and CVD coatings provide them with extreme toughness and wear resistance.

Case Studies

Forming & Molding Case Studies

Download the case studies to get an insight and learn about the true performance of our multipurpose and premium coating solutions in various forming applications.

38 pages | 30 minutes well spent

Ionbond Forming Molding Portrait
Ionbond CVD 29 sample

Highly desirable properties and flexibility

The advantages of CVD processes include:

  • Advantageous residual stress profile which allows the deposition of thick CVD coatings (+20 µm)
  • CVD coatings with extreme toughness and unrivaled impact fatigue resistance
  • High adhesion of CVD coating on tools due to interdiffusion between coating and base material
  • Tools to be coated do not require rotation within the retort
  • The possibility to coat complex geometries, including certain inner diameters
  • Excellent coating uniformity, independent of tool geometry

CVD technology enables the production of titanium (Ti) or chome (Cr) based coatings in form of nitrides (N), carbides (C) and carbonitrides (CN). In addition, high-quality aluminum oxide (Al2O3) layers can be created, both in the α and κ phase. These CVD coatings are almost always deposited as multilayers, such as TiC/TiN, TiN/TiCN/TiN, TiCN/Al2O3 or TiCN/Al2O3/TiN, where the layer combination is engineered to meet the demands of a specific forming application. Coating thickness typically ranges from 5 µm to 12 µm, but in some cases coatings can be as thick as 20 µm or more.

The various CVD Ti coating structures and their benefits

TiC

When deposited by CVD, a TiC layer provides a low coefficient of friction, high toughness and high resistance against abrasive wear. This is beneficial for forming applications, such as cold forming ferritic and austenitic stainless steel, high strength low-allow steels (HSLA), advanced high strength steels (AHSS) and steel workpieces with a thickness > 2 mm.

TiN/TiC/TiN multilayer or TiCN solid solution

The combination of individually deposited TiN or TiC coatings in a TiN/TiC/TiN multilayer structure or in a TiCN solid solution further increases the performance in forming applications. TiCN is the preferred coating solution for light to medium metal forming applications involving stainless steels, HSLA and steel workpieces with a thickness > 3 mm. The multilayer CVD coating TiN/TiC/TiN reveals extreme toughness under impact loading and superior adhesion between the coating and the tool, which makes it an excellent choice for cold forging steels and warm or hot extrusion of ceramics or non-ferrous alloys.

Al2O3

The CVD deposition of Al2O3 can provide further improvement in terms of oxidation resistance and hot hardness for aggressive conditions, such as those in high-temperature forming applications. Al2O3 can be deposited in α phase (thermodynamically stable) or κ phase (metastable), and is often deposited on TiC or TiCN in a multilayer structure. An Al2O3 layer exhibits excellent thermal stability, chemical inertness, and a high resistance against corrosion, abrasive wear and adhesive wear. That  makes it the leading coating solution for hot extrusion of both ferrous and non-ferrous alloys.

Multilayer TiCN/Al2O3/TiN coating

Finally, a multilayer TiCN/Al2O3/TiN coating combines the main advantages of the individual layers. The TiCN bond coat ensures a high wear resistance and provides excellent adhesion to the tool. The Al2O3 layer exhibits excellent thermal stability, high hot hardness and extreme wear resistance. And the TiN top layer can be used for wear detection during service life of the coating forming tool.

Coating Technology CVD 2022

Suitable for many tool steels with post-coating heat treatment

Thermal CVD is a heat-activated process where the tools to be coated are heated to an appropriate temperature and exposed to one or more solid or liquid precursors. For instance, the halides TiCl4, AlCl3, or CrCl3. In combination with certain reactive gases such as H2, N2 or CH4, the halide precursors react on the tool surface to produce the desired coating. The schematic you see shows a CVD process. By combining the precursors TiCl4 and CH4 at 1,000 °C, a TiC coating is created.

TiCl4 + CH4TiC + 4 HCl

The typical process temperature for CVD coatings is between 900 °C and 1,050 °C for high temperature (HT) CVD and between 720 °C and 900 °C for the moderate temperature (MT) CVD processes from IHI Bernex. These high process temperatures might make certain base materials unsuitable for CVD, or require a post-coating heat treatment of the tools. The necessity of a heat treatment should not, however, discourage the use of CVD processes on tool steels. The CVD coating is unaffected by the post-coating heat treatment. When the heat treatment is carried out under vacuum conditions, the CVD coating retains its mechanical properties and adhesion to the tool.

Table base materials FMT Applications CVD

Selecting heat treatment parameters to match the base material

By carefully selecting the CVD coating and heat treatment parameters, the surface engineers from Ionbond help prevent excessive thermal distortion of the coated tools after heat treatment. This can be done for common cold and hot work tool steels and high-speed steels, see table. Austenitic stainless steel can even be processed by CVD without a need for post-coating heat treatment, since it does not undergo a phase transformation below the CVD process temperature. Another exception is heat-treated martensitic stainless steel. This can be also processed at a lower temperature, making it possible to use MT-CVD to retain the core hardness in the range of 35 to 40 HRC.

Table: Overview of base materials for forming and molding tool applications, common types of CVD coatings and required post-coating heat treatment.

Widely used Ionbond™ CVD coatings

Forming & Molding
IB CVD 10 Ti CN transp

Ionbond™ CVD 10

Traditional CVD Coating for use in metal forming applications

Ionbond™ CVD 10 is a CVD TiCN coating with a high hardness, good toughness and wear resistance, and a lower coefficient of friction than other CVD coatings like Ionbond™ CVD 13. This combination of properties makes Ionbond™ CVD 10 a preferred product over Ionbond™ CVD 13 for open tolerance tooling used in light to medium metal forming applications involving stainless steels, steel alloys with thicknesses greater than 3 mm, and high strength low alloy (HSLA) materials.

Ionbond™ CVD 10 can be deposited between 800 and 1000°C. Therefore it is only recommended for tool materials compatible with the CVD process. In addition, dimensional change will occur on tool steel materials coated with Ionbond™ 10. Therefore, sufficient dimensional tolerances are required to accommodate the expected dimensional change. The broader deposition range for Ionbond™ CVD 10, as compared to that for Ionbond™ CVD 13 and Ionbond™ CVD 02, allow for it to be used on tool steels like S7 (1.2355) or A2 (1.2363), which are not compatible with the deposition process for Ionbond™ CVD 13 or Ionbond™ CVD 02.

Read more
Forming & Molding
Cold forging punch

Ionbond™ CVD 13

Traditional CVD Coating for use in metalforming applications

High hardness, toughness, and wear resistance make Ionbond™ CVD 13 a versatile product for open tolerance tooling used in light to medium metal
forming applications. In addition, the toughness under impact loading makes Ionbond™ CVD 13 an excellent product for open tolerance tooling used in cold forging and fastener trim die applications.

Since Ionbond™ CVD 13 is deposited by means of the CVD process, they can be deposited onto tools with small openings, complex geometries and long aspect ratios (> 1:1). This capability makes it a viable solution for wire drawing, warm and hot extrusion, and some plastic molding injection nozzle applications. Ionbond™ CVD 13 is an excellent choice for ceramic or non steel tool materials in order to promote superior coating adhesion.

Ionbond™ CVD 13 is deposited at 1000 °C. Therefore it is only recommended for tool materials compatible with the CVD process. In addition, dimensional change will occur on tool steel materials coated with Ionbond™ CVD 13. Therefore, sufficient dimensional tolerances are required to accommodate the expected dimensional change.

Read more
Forming & Molding
Ionbond CVD 29 transp

Ionbond™ CVD 29

Aluminum oxide coating for high temperature forming applications

Ionbond™ CVD 29 Al2O3 is a multi-layered CVD coating engineered to be able to cope with the aggressive conditions present in high temperature forming applications. Ionbond™ CVD 29 Al2O3 exhibits excellent thermal stability, chemical inertness, and high wear resistance, which makes it the leading solution for hot extrusion applications for both ferrous and non-ferrous alloys.
Additionally, the thermal stability, density, and corrosion resistance of Ionbond™ CVD 29 makes it an ideal solution for open tolerance tools used in aluminum casting applications where sticking of aluminum is the primary cause of downtime.

Ionbond™ CVD 29 is deposited at 1000 °C. Therefore it is only recommended for tool materials compatible with the CVD process. Dimensional change will occur on tool steel materials coated with Ionbond™ CVD 29, so sufficient dimensional tolerances are required to accommodate the expected dimensional change.

Read more
Forming & Molding
Orbital forming tool white

Ionbond™ CVD 62

Premium CVD coating for use in metalforming applications

Ionbond™ CVD 62 couples the high hardness, toughness and wear resistance of CVD deposited TiC with the ultra low coefficient of friction of MoS2 solid lubricant coating. The result is a more efficient product for open tolerance tooling used in metal forming applications where sliding friction is the root cause of tool failure. Ionbond™ CVD 62 provides excellent performance in the forming of ferritic and austenitic stainless steels, high strength low alloy (HSLA) and advanced high strength steels (AHSS), steel alloy work pieces with thicknesses of more than 2mm, nickel alloys and titanium.

The high toughness and ultra low coefficient of friction of Ionbond™ CVD 62 make it an excellent solution for open tolerance tools used in piercing applications. Ionbond™ CVD 62 is particularly tailored to materials with high work hardening or spring back properties.

The TiC component of Ionbond™ CVD 62 is deposited at 1000°C. Therefore, it is only recommended for tool materials compatible with the elevated temperatures. Due to the fact that tool steel will undergo dimensional changes, sufficient dimensional tolerances are required or dimensioning has to be adapted to compensate for the expected changes. Tempered tools need to be heat treated after coating in order to restore the desired hardness of the tool material.

Read more

Get in touch

Discuss your challenges with Tobias Brögelmann

Dr. Ing. Tobias Brögelmann, Global Segment Manager Forming and Molding Tools, will be glad to support you.

We will get back to you as soon as possible.

Broegelmann Tobias 2021

Dr. Ing. Tobias Brögelmann

Global Segment Manager Forming and Molding

Coating applications for forming & molding tools

Ionbond™ PVD, PACVD, and CVD coatings are proven to improve performance in tools for a wide variety of forming and molding applications.

Coating solutions for Cold Forming

Cold Forming

Stable, reliable processes, low scrap rates and superb product integrity

Read more
Ionbond Forming Molding Portrait

Hot forming

Improve tool life and product quality by increasing high hot hardness, thermal stability and galling resistance

Read more
Ionbond Forming Molding Portrait

Plastic molding

Improve tool life and reduce scrap rates by improving product release, details and finish

Read more
Ionbond Forming Molding Portrait

Plasma Nitriding

Boost the performance of your forming application

Read more