Tribobond™ 31 Cr2N
High impact resistant coating with smooth surface for high temperatures
Ionbond’s Tribobond™ 31 Cr2N coating possesses a good combination of properties; high hardness (approaching three times that of hard chromium), excellent toughness, good wear resistance and high impact fatigue resistance. Tribobond™ 31 has a high temperature resistance, which makes it a good candidate for higher temperature applications such as turbochargers, piston rings and other mechanical components used at elevated temperatures.
Tribobond™ 31 Cr2N features lower residual stress than many other coatings, allowing for the deposition of thicker layers. This makes it an ideal and environmentally friendly alternative to hard chromium Cr6+ electroplating. Coated components require no grinding back to size since the coating is very thin with a high thickness uniformity.
Tribobond™ 31 Cr2N protects against sliding and impact fatigue, oxidation, fretting and adhesive wear.
- Aerospace components
- Turbocharger and engine components
- Hard chrome replacement
Technical data |
|
|---|---|
Material |
Cr2N |
Coating thickness |
2 - 5 μm |
Service Temp. |
700 °C |
Deposition Temp. |
180 - 200 °C |
Hardness HV 0.05 |
2500 - 2900 |
Deposition method |
PVD Sputtering |
Friction vs. steel, dry |
0.55 |
Color |
Metallic silver |