Coating	Material	Technology	Thickness range [µm]	Microhardness, HV	Friction vs. Steel (dry)	Service Temperature	Process Temperature	Color	Application Reference	Nanohardness, HV 0.005
Tribobond™ 01	TiN	PVD Arc	1.5 - 5μm	2000 - 2500	<0.55 dry vs. steel	500°C	150 - 500°C	Gold	-	-
Tribobond™ 15	TiAICrN	PVD Arc	2 - 5μm	2500 - 3000	<0.6 dry vs. steel	850°C	300 - 500°C	Dark-Grey	-	-
Tribobond™ 30	CrN	PVD uBM/Arc	2 - 40μm	1800 - 2300 uBM/2000 - 2800 Arc	<0.55	700°C	150 - 400°C	Silver	General wear resistance, low process temperature	-
Tribobond™ 31	Cr2N	PVD Sputter	2 - 5μm	2500 - 2900	<0.55	700°C	180 - 200°C	Silver	General wear resistance, low process temperature	-
Tribobond™ 40	Cr + a-C:H:W	PVD UBM	1 - 10μm	1000 - 1800	<0.2	350°C	<200°C	Grey	-	-
Tribobond™ 41	Cr + a-C:H:W + a-C:H	PVD UBM + PACVD	1 - 8μm	-	<0.1	300°C	<200°C	Black	-	2000 - 2800
Tribobond™ 42	Cr + CrN + CrWC + a-C:H	PVD UBM + PACVD	1 - 8μm	2000 - 2800	<0.1	300°C	200 - 250°C	Black	-	-
Tribobond™ 46	Cr + CrN + a-C:H:W	PVD UBM	1 - 8μm	1000 - 1800	< 0.1	350°C	200 - 250°C	Grey	-	-
Tribobond™ 48	Cr + ta-C	PVD UBM + PVD Arc	0.5 - 1.5μm	4000 - 8000	< 0.1	400°C	<200°C	Black	-	-
Tribobond™ 49	Cr + CrWC + ta-C	PVD UBM + PVD HIPIMS	0.5 - 1.5μm	3000 - 5000	< 0.1	400°C	<200°C	Black	-	-
Tribobond™ 55	Cr + a-C:H:X	PVD sputtering	1 - 8μm	750 - 900	<0.05 (vacuum)	350°C	200°C	Black	Low friction for vacuum and dry gas environment	-
Tribobond™ 56	Cr + CrN + CrWC+ a-C:H:X	PVD UBM + PVD Arc	1 - 8µm	750 - 900	< 0.05 (hydrogen, vacuum, dry gas)	350 °C	200 °C	Black	Hydrogen fuel injection and compressor components	-

Questions?

Discuss your challenges with André Hieke

André Hieke, Global Segment Manager Automotive, will be glad to support you.

We will get back to you as soon as possible

André Hieke

Global Segment Manager Automotive