Ionbond™ 62 TiCN + MoS2

Premium PVD coating for use in metal forming applications

Ionbond™ 62 combines the hardness, toughness and wear resistance of PVD TiCN with the ultra low coefficient of friction of a solid lubricant coating to produce a more efficient product in metal forming applications where sliding friction is the root cause of tool failure. Ionbond™ 62 provides excellent performance in forming applications involving ferritic and austenitic stainless steels, high strength low alloy (HSLA) and advanced high strength steels (AHSS), galvanized, pre-painted, or coated materials, copper alloys, nickel alloys and titanium. Depending on the application or the tool material, Ionbond™ 62 may need to be combined with nitriding in order to achieve maximum performance.

The characteristics of Ionbond™ 62 make it ideal for applications where high friction results in high extraction forces for tools. It is ideally used for piercing, particularly in thick gauge or high strength material, powdered metal compaction and plastic molding ejector pin applications.

The TiCN component included in Ionbond™ 62 is deposited at 425 °C. Therefore it is recommended that tool materials be tempered above 450 °C in order to avoid softening or dimensional changes.

Technical data  
Material TiCN + MoS2
Coating thickness 2 - 5 μm
Service Temp. 500 °C
Deposition Temp. 425 °C / 150 °C
Hardness HV 0.05 3000 + 2000
Deposition method PVD arc / Sputtering
Friction vs. steel, dry 0.03 - 0.06
Color grey