Tetrabond™ Plus ta-C

Smooth ta-C coating

Tetrabond™ Plus is an advanced ta-C coating for machining non-ferrous metals as well as composite and plastic materials. With an sp3 content of 80 – 90%, it reaches a hardness of over 5000 HV.

The thin, smooth, and extremely hard coating is designed to maintain maximum cutting edge sharpness in machining abrasive materials, such as graphite, composite materials with glass or carbon fibre, glass reinforced PCB materials, and high Si content aluminum alloys. Tetrabond™ Plus excels in cutting soft noble metals like gold, silver and copper as well as lead-containing and lead-free bronzes and brass alloys. Its low thickness, very low coefficient of friction, and anti-stick properties makes Tetrabond™ Plus excellent in machining a wide range of plastics and sticky materials where it avoids the build-up of material on the sharp cutting edge.

Alternative to CVD Diamond coatings for a wide range of tools

Tetrabond™ Plus can be applied to HSS, cemented carbide, and brazed tools, regardless of geometry. It can be stripped in a proprietary process without attacking the tool base material and reapplied after regrinding, making the best use of expensive cutting tools.

Tetrabond™ Plus is an economical solution for machining difficult materials, reducing the need for expensive PCD inserts & diamond coated tools.

Technical data

 

Material

ta-C

Coating thickness

0.5 - 1.5 μm

Service Temp.

500 °C

Deposition Temp.

below 180 °C

Hardness HV 0.05

> 5000

Adhesion

very good - typically class 1

Deposition method

proprietary PVD Arc

Friction vs. steel, dry

< 0.1

Color

dark grey